Stafloor EP Finish

-Universal application.
-Low odour.
-Layer thickness from 0.5 to 5 mm.
-Can be used under high mechanical loads.
-Chemically resistant to diluted acids and alkalis, salts and their solutions, many solvents, fuels, grease, oils, cleaning, washing, wetting and disinfecting agents, as well as food products.
-Impermeable to liquids.
-The cured coating is physiologically safe.
-A non-slip coating can be made (with sand broadcast).

Stafloor EP Finish creates mechanically and chemically resistant floor coatings that meet high aesthetic requirements, used as floor coatings in industrial, warehouse, exhibition and retail premises, at paper mills, food-industry enterprises, pharmaceutical facilities, nuclear power plants, and at sites with heavy pedestrian, forklift and vehicle traffic.

Purpose	Mechanically and chemically resistant floor coatings: roller-applied, self-levelling, self-levelling mortar, and anti-slip with sand broadcast
Type	Two-component solvent-free epoxy coating
Colour	approx. RAL 7032 and RAL 7035; other colours on request. Prolonged UV exposure may change the shade
Layer thickness	Roller — 0.5 mm. Self-levelling coating — 0.5–1.5 mm. Self-levelling mortar — 1.5–5 mm
Packaging	Kit 25.0 kg: component A — 20.0 kg, component B — 5.0 kg
Mixing ratio	A : B = 100 : 25 by weight
Density of the mix	approx. 1.6 g/cm³ (DIN 53217)
Shore D hardness	64 (DIN EN ISO 868, 7 days at +23 °C)
Compressive strength	52 N/mm² (DIN EN ISO 604, 7 days at +23 °C)
Abrasion	50 mg per 1000 cycles (1000 g load, CS 10 wheel; ASTM D 4060, Taber abraser)
Wear by abrasion	approx. 6 cm³ per 50 cm² (DIN 52108)
Slip resistance	R11/V4 and R12/V6 with sand broadcast (ZH 1/571, DIN 51130); the class depends on the sand grain size
Heat resistance	continuous up to +80 °C; short-term up to +100 °C dry and up to +80 °C wet
Chemical resistance	dilute acids and alkalis, salts and their solutions, many solvents, fuel, greases, oils, cleaning, washing and disinfecting agents, foodstuffs
Consumption	approx. 0.80 kg/m² at 0.5 mm (roller); approx. 1.60 kg/m² at 1 mm (self-levelling coating)
Pot life	20 minutes at +20 °C
Foot traffic	after 24 hours at +20 °C
Next coat	after 24 hours, and not later than 72 hours
Full cure	7 days
Application temperature	from +10 °C to +30 °C (substrate and air)
Relative humidity	max. 80 %
Dew point	substrate temperature at least 3 °C above the dew point
Substrate requirements	compressive strength min. 25 N/mm², pull-off min. 1.5 N/mm², moisture max. 4 % by the CM method
Tool cleaning	P-4 thinner; fully cured material can be removed mechanically only
Shelf life	12 months in unopened packaging at +3…+30 °C